The oxygen barrier properties of Soarnol depend on ethylene content and humidity. The most suitable grade for a given purpose can be determined according to application and manufacturing process.
| D2908 | DT2904 | DC3212 | DC3203 | E3808 | ET3803 | A4412 | AT4403 | ||
|---|---|---|---|---|---|---|---|---|---|
| Technical document |  |
|
|
|
|
|
|
|
|
 |
|
|
|
|
|
|
|
||
| Ethylene content | mol% | 29 | 32 | 38 | 44 | ||||
| Density | g/cm3 | 1.21 | 1.19 | 1.17 | 1.14 | ||||
| Melting point *1 | deg C | 188 | 183 | 173 | 164 | ||||
| Crystallization temp. *1 | deg C | 163 | 160 | 152 | 144 | ||||
| Glass transition temp. *1 | deg C | 62 | 61 | 58 | 55 | ||||
| MFR *2 | g/10min | 8 | 4 | 12 | 3.8 | 8 | 3.2 | 12 | 3.5 |
| Apparent melt viscosity *3 | 210deg C poise | 9000 | 24000 | 5500 | 24000 | 9000 | 24000 | 5500 | 20000 |
| 210deg C Pa·s | 900 | 2400 | 550 | 2400 | 900 | 2400 | 550 | 2000 | |
| 230deg C poise | 5000 | 13000 | 2500 | 13000 | 5000 | 12000 | 2500 | 10000 | |
| 230deg C Pa·s | 500 | 1300 | 250 | 1300 | 500 | 1200 | 250 | 1000 | |
| OTR*4 | cc·20µm/m2·day·atm | 0.4 | 0.5 | 0.7 | 1.5 | ||||
| cm3·20µm/m2·24hrs·MPa | 4 | 5 | 7 | 15 | |||||
| Manufacturing process | Blown film |  |
|
|
|
||||
| Cast film | |
|
|
|
|||||
| Sheet | |
|
|
|
|||||
| Bottle | |
|
|
||||||
| Pipe | |
|
|
|
|||||
*1 Measured with DSC.
*2 210deg C(410deg F), 230deg C(446deg F)
*3 Measured with melt flow tester which has 1mm¢*10mmL nozzle and 490N{50kgf}load.
*4 20deg C*65%RH The data in the table are in house standards and not guaranteed values.
*5 23deg C*70%RH
Special Grade
| Thermoforming grades | BX6804B | （85KB） |
|---|---|---|
| TF2905B | （84KB） |
|
| Pipe Grades | D2908H4 | （84KB） |
| DC3205HB | （83KB） |
|
| Purging resin | PG505 | （77KB） |
| Regrind agent | RG100 | （77KB） |
| Flex-crack resistance grades | Please contact us | |
| Retort Grades | Please contact us | |
| Plastic fuel tank grades | Please contact us | |
Global navigation